Fil d'acier inoxydable
COMPOSITION CHIMIQUE. ANALYSE DE COULÉE (% EN MASSE) EN-ISO 6931-1
| ACIER INOXYDABLE À RESSORT | C | Si max. | Mn max. | P max. | S max. | Cr | Mo | Ni | Autres éléments | ||
| Désignation symbolique | Désignation numérique | AISI | |||||||||
| X10CrNi18-8 (NS / HS) | 1.4310 | 302 | 0,05 - 0,15 | 2,00 | 2,00 | 0,045 | 0,015 | 16,0 - 19,0 | ≤ 0,80 | 6,0 - 9,5 | N ≤ 0,11 |
| X5CrNiMo17-12-2 | 1.4401 | 316 | ≤ 0,07 | 1,00 | 2,00 | 0,045 | 0,015 | 16,5 - 18,5 | 2,00 - 2,50 | 10,0 - 13,0 | N ≤ 0,11 |
| X7CrNiAl17-7 | 1.4568 | 631 | ≤ 0,09 | 0,70 | 1,00 | 0,040 | 0,015 | 16,0 - 18,0 | - | 6,5 - 7,8 | Al: 0,70 - 1,50 |
| X5CrNi18-10 (NS / HS) | 1.4301 | 304 | ≤ 0,07 | 1,00 | 2,00 | 0,045 | 0,015 | 17,5 - 19,5 | - | 8,0 - 10,5 | N ≤ 0,11 |
| X1NiCrMoCu25-20-5 | 1.4539 | 904L | ≤ 0,020 | 0,70 | 2,00 | 0,030 | 0,010 | 19,0 - 21,0 | 4,0 - 5,0 | 24,0 - 26,0 | N ≤ 0,15 |
COMPOSITION CHIMIQUE (ANALYSE COULÉE D'ACIERS INOXYDABLES MARTENSITIQUES ET DURCIS PAR PRÉCIPITATION, D'ACIERS INOXYDABLES FERREUX, D'ACIERS INOXYDABLES AUSTÉNITIQUES), référence à la norme EN 10088-3
| ACIER INOXYDABLE À USAGE GÉNÉRAL | en masse | ||||||||||||
| Symbolique | Numérique | AISI | C | Si max. | Mn max. | P max. | S | N max. | Cr | Cu | Mo | Ni | Ti |
| Aciers martensitiques | |||||||||||||
| X30Cr13 | 1.4028 | 420 | 0,26 - 0,35 | 1,00 | 1,50 | 0,040 | ≤ 0,03 | - | 12,00- 14,00 | - | - | - | - |
| Aciers ferritiques | |||||||||||||
| X6Cr17 | 1.4016 | 430 | ≤ 0,08 | 1,00 | 1,00 | 0,04 | ≤ 0,030 | - | 16,00 - 18,00 | - | - | ≤ 0,75 | - |
| Aciers austénitiques | |||||||||||||
| X2CrNi18-9 | 1.4307 | 304L | ≤ 0,03 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 17,50 - 19,50 | - | - | 8,00 - 10,00 | - |
| X5CrNi18-10 | 1.4301 | 304 | ≤ 0,07 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 17,00 - 19,50 | - | - | 8,00 - 10,50 | - |
| X8CrNiS18-9 | 1.4305 | 303 | ≤ 0,10 | 1,00 | 2,00 | 0,045 | 0,15 - 0,35 | 0,11 | 17,00 - 19,00 | ≤ 1,00 | - | 8,00 - 1,00 | - |
| X2CrNiMo17-12-2 | 1.4401 | 316L | ≤ 0,03 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 16,50 - 18,50 | - | 2,00 - 2,50 | 10,00 - 13,00 | - |
| X2CrNiMo18-14-3 | 1.4435 | 316L | ≤ 0,03 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 17,00 - 19,00 | - | 2,50 - 3,00 | 12,50 - 15,00 | - |
| X5CrNiMo17-12-2 | 1.4401 | 316 | ≤ 0,07 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 16,50 - 18,50 | - | 2,00 - 2,50 | 10,00 - 13,00 | - |
| X3CrNiMo17-13-3 | 1.4436 | 316 | ≤ 0,05 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 16,50 - 18,50 | - | 2,50 - 3,00 | 10,50 - 13,00 | - |
| X6CrNiMoTi17-12-2 | 1.4571 | 316Ti | ≤ 0,08 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | - | 16,50 - 18,50 | - | 2,00 - 2,50 | 10,50 - 13,50 | 5 x C - 0,70 |
| X3CrNiCu18-9-4 | 1.4567 | 304Cu | ≤ 0,04 | 1,00 | 2,00 | 0,045 | ≤ 0,030 ³⁾ | 0,11 | 17,00 - 19,00 | 3,00 - 4,00 | - | 8,50 - 10,50 | - |
| X8CrMnCuNB17-8-3 | 1.4597 | 204Cu | ≤ 0,10 | ≤ 2,00 | 6,50 - 8,50 | ≤ 0,040 | ≤ 0,015 | - | 16,00 - 18,00 | 2,00 - 3,50 | ≤ 1,00 | ≤ 2,00 | - |
| X12CrNi23-13 | 1,4833 | 3095 | ≤ 0,08 | ≤ 0,75 | ≤ 2,00 | ≤ 0,040 | ≤ 0,015 | - | 22,00-24,00 | - | - | 12,00-14,00 | - |
| X8CrNi25-21 | 1,4845 | 310S | ≤ 0,08 | ≤ 1,50 | ≤ 2,00 | ≤ 0,040 | ≤ 0,015 | - | 24,00-26,00 | - | - | 19,00-22,00 | - |
| X15CrNiSi25-21 | 1.4841 | 314 | 0,02 | 1,50-3,00 | ≤ 0,02 | ≤ 0,045 | ≤ 0,015 | - | 24,00-26,00 | - | - | 19,00-22,00 | - |
| ACIER INOXYDABLE À RESSORT | |||||
| Désignation symbolique | EUROPÉENNE EN 10270-3 | AISI | É.-U. ASTM | JAPON JIS | CHINE |
| X10CrNi18-8 | 1.4310 | 302NS | AISI 302 NS | SUS 302-WPB | - |
| X10CrNi18-8 | 1.4310 | 302HS | AISI 302 HLS | - | - |
| X5CrNiMo17-12-2 | 1.4401 | 316 | AISI 316 | SUS 316-WPA | - |
| X7CrNiAl17-7 | 1.4568 | 631 | AISI 631 | SUS 631J1-WPC | - |
| X5CrNi18-10 (NS / HS) | 1.4301 | 304 | AISI 304 | SUS 304-WPB | - |
| X1NiCrMoCu25-20-5 | 1.4539 | 904L | - | - | - |
| ACIER INOXYDABLE À USAGE GÉNÉRAL | |||||
| Symbolique | Numérique EN 10088-3 | AISI | É.-U. ASTM | JAPON JIS | CHINE |
| Aciers martensitiques | |||||
|---|---|---|---|---|---|
| X30Cr13 | 1.4028 | 420 | |||
| Aciers ferritiques | |||||
| X6Cr17 | 1.4016 | 430 | |||
| Aciers austénitiques | |||||
| X2CrNi18-9 | 1.4307 | 304L | |||
| X5CrNi18-10 | 1.4301 | 304 | |||
| X8CrNiS18-9 | 1.4305 | 303 | |||
| X2CrNiMo17-12-2 | 1.4404 | 316L | |||
| X2CrNiMo18-14-3 | 1.4435 | 316L | |||
| X5CrNiMo17-12-2 | 1.4401 | 316 | |||
| X3CrNiMo17-13-3 | 1.4436 | 316 | |||
| X6CrNiMoTi17-12-2 | 1.4571 | 316Ti | |||
| X3CrNiCu18-9-4 | 1.4567 | 304Cu | |||
| X8CrMnCuNB17-8-3 | 1.4597 | 204Cu | |||
| X12CrNi23-13 | 1.4833 | 3095 | |||
| X8CrNi25-21 | 1.4845 | 310S | |||
| X15CrNiSi25-21 | 1.4841 | 314 | |||
RÉSISTANCE À LA TRACTION EN CONDITIONS DE TRÉFILAGE Acier inoxydable pour ressorts EN 10270-3
| Résistance à la traction (MPa) pour les types d'aciers suivants | |||||||||||||
| 1.4310 | 1.4401 | 1.4568 | 1.4301 | 1.4539 | |||||||||
| Diamètre nominal mm d | 302NS | 302HS | 316 | 631 | 304 NS | 304 HS | 904L | ||||||
| min. | max. | min. | max. | min. | max. | min. | max. | min. | min. | max. | min. | max. | |
| d ≤ 0,20 | 2200 | 2530 | 2350 | 2710 | 1725 | 1990 | 1975 | 2280 | 2000 | 2150 | 2300 | 1600 | 1840 |
| 0,20 < d ≤ 0,30 | 2150 | 2480 | 2300 | 2650 | 1700 | 1960 | 1950 | 2250 | 1975 | 2050 | 2280 | 1550 | 1790 |
| 0,30 < d ≤ 0,40 | 2100 | 2420 | 2250 | 2590 | 1675 | 1930 | 1925 | 2220 | 1925 | 2050 | 2220 | 1550 | 1790 |
| 0,40 < d ≤ 0,50 | 2050 | 2360 | 2200 | 2530 | 1650 | 1900 | 1900 | 2190 | 1900 | 1950 | 2190 | 1500 | 1750 |
| 0,50 < d ≤ 0,65 | 2000 | 2300 | 2150 | 2480 | 1625 | 1870 | 1850 | 2130 | 1850 | 1950 | 2130 | 1450 | 1670 |
| 0,65 < d ≤ 0,80 | 1950 | 2250 | 2100 | 2420 | 1600 | 1840 | 1825 | 2100 | 1800 | 1850 | 2070 | 1450 | 1670 |
| 0,80 < d ≤ 1,00 | 1900 | 2190 | 2050 | 2360 | 1575 | 1820 | 1800 | 2070 | 1775 | 1850 | 2050 | 1400 | 1610 |
| 1,00 < d ≤ 1,25 | 1850 | 2130 | 2000 | 2300 | 1550 | 1790 | 1750 | 2020 | 1725 | 1750 | 1990 | 1350 | 1560 |
| 1,25 < d ≤ 1,50 | 1800 | 2070 | 1950 | 2250 | 1500 | 1730 | 1700 | 1960 | 1675 | 1750 | 1930 | 1350 | 1560 |
| 1,50 < d ≤ 1,75 | 1750 | 2020 | 1900 | 2190 | 1450 | 1670 | 1650 | 1900 | 1625 | 1650 | 1870 | 1300 | 1500 |
| 1,75 < d ≤ 2,00 | 1700 | 1960 | 1850 | 2130 | 1400 | 1610 | 1600 | 1840 | 1575 | 1650 | 1820 | 1300 | 1500 |
| 2,00 < d ≤ 2,50 | 1650 | 1900 | 1750 | 2020 | 1350 | 1560 | 1550 | 1790 | 1525 | 1550 | 1760 | 1300 | 1500 |
| 2,50 < d ≤ 3,00 | 1600 | 1840 | 1700 | 1960 | 1300 | 1500 | 1500 | 1730 | 1475 | 1550 | 1700 | 1300 | 1500 |
| 3,00 < d ≤ 3,50 | 1550 | 1790 | 1650 | 1900 | 1250 | 1440 | 1450 | 1670 | 1425 | 1450 | 1640 | 1300 | 1500 |
| 3,50 < d ≤ 4,25 | 1500 | 1730 | 1600 | 1840 | 1225 | 1410 | 1400 | 1610 | 1400 | 1450 | 1610 | 1250 | 1440 |
| 4,25 < d ≤ 5,00 | 1450 | 1670 | 1550 | 1790 | 1200 | 1380 | 1350 | 1560 | 1350 | 1350 | 1560 | 1250 | 1440 |
| 5,00 < d ≤ 6,00 | 1400 | 1610 | 1500 | 1730 | 1150 | 1330 | 1300 | 1500 | 1300 | 1350 | 1500 | 1250 | 1440 |
| 6,00 < d ≤ 7,00 | 1350 | 1560 | 1450 | 1670 | 1125 | 1300 | 1250 | 1440 | 1250 | 1300 | 1440 | 1200 | 1380 |
| 7,00< d ≤ 8,50 | 1300 | 1500 | 1400 | 1610 | 1075 | 1240 | 1250 | 1440 | 1200 | 1300 | 1380 | 1150 | 1330 |
| 8,50 < d ≤ 10,00 | 1250 | 1440 | 1350 | 1560 | 1050 | 1210 | 1250 | 1440 | 1175 | 1250 | 1360 | - | - |
REMARQUE - Possibilité de fourniture de d ≥ 14 mm hors norme, sur demande commerciale.
INTERVALLE DE LA RÉSISTANCE À LA TRACTION POUR CHAQUE ENSEMBLE UNITAIRE (BOBINE, ENSEMBLE) EN 10270-3
| Diamètre du fil d (mm) | Intervalle maximum |
| d ≤ 1,50 | 100 |
| 1,50 < d ≤ 10,00 | 70 |
ACIER POUR DIFFÉRENTES APPLICATIONS
| Symbolique | Numérique EN 10088-3 | AISI | Résistance [N/mm2] | |
| État recuit | État demi-dur | |||
| X6Cr17 | 1.4016 | 430 | ≤ 640 | 650-900 |
| X2CrNi18-9 | 1.4307 | 304L | ≤ 640 | 650-900 |
| X5CrNi18-10 | 1.4301 | 304 | ≤ 640 | 650-900 |
| X8CrNiS18-9 | 1.4305 | 303 | ≤ 590 | 600-700 |
| X3CrNiCu18-9-4 | 1.4567 | 304Cu | ≤ 600 | 600-700 |
QUALITÉ SUPERFICIELLE EN-ISO 6931-1
La surface du Fil d'acier inoxydable doit être lisse et, dans la mesure du possible, exempte d'égratignures, de piqûres et autres défauts superficiels susceptibles de compromettre l’utilisation du fil. L'essai de torsion alternative est une méthode qui permet de révéler les discontinuités superficielles.
Si le fil est destiné à la fabrication de ressorts utilisés pour de fortes contraintes, les exigences spéciales en rapport avec la qualité de surface et les tests peuvent faire l'objet d'accord selon les indications préalables du client au moment de l'offre ou de la commande.
| Finitions de surface pour Fil d'acier inoxydable destinés aux ressorts : | |
| Savon S-Co | Revêtement standard |
| Savon spécial SS-Co/ S-Co+ | Améliore la formation du ressort |
| Brillante | Aspect de surface brillant, même s'il existe une légère couche de savon |
| Sans polissage | Tréfilage humide |
| Nickelage mat | Tréfilage à sec |
| Nickelage brillant | Tréfilage humide |
QUALITÉ SUPERFICIELLE EN 10088-3
De légères irrégularités de surface sont tolérées, inhérentes au processus de fabrication. Si nécessaire, des exigences plus précises quant à la qualité de surface peuvent faire l'objet d'un accord au moment de la commande, sur la base de la norme EN 10221.
TOLÉRANCES EN DIAMÈTRE EN-ISO 6931-1
| Diamètre nominal d (mm) | Tolérances en diamètre (mm) | |
| Tólerances en diamètre mm perche ou bobines | ||
| T14 | T15 | |
| d ≤ 0,20 | ± 0,005 | ± 0,004 |
| 0,20 < d ≤ 0,25 | ± 0,005 | ± 0,004 |
| 0,25 < d ≤ 0,40 | ± 0,008 | ± 0,005 |
| 0,40 < d ≤ 0,64 | ± 0,008 | ± 0,005 |
| 0,64 < d ≤ 0,80 | ± 0,010 | ± 0,008 |
| 0,80 < d ≤ 1,00 | ± 0,010 | ± 0,008 |
| 1,00 < d ≤ 1,60 | ± 0,015 | ± 0,010 |
| 1,60 < d ≤ 2,25 | ± 0,015 | ± 0,010 |
| 2,25 < d ≤ 3,19 | ± 0,020 | ± 0,015 |
| 3,19 < d ≤ 4,00 | ± 0,020 | ± 0,015 |
| 4,00 < d ≤ 4,50 | ± 0,025 | ± 0,020 |
| 4,50 < d ≤ 6,00 | ± 0,025 | ± 0,020 |
| 6,00 < d ≤ 6,25 | ± 0,025 | ± 0,020 |
| 6,25 < d ≤ 7,00 | ± 0,030 | ± 0,025 |
| 7,00 < d ≤ 9,00 | ± 0,030 | ± 0,025 |
| 9,00 < d ≤ 10,00 | ± 0,035 | ± 0,030 |
REMARQUE 1 - Possibilité de fourniture de d ≥ 14 mm hors norme, sur demande commerciale.
REMARQUE 2 - T15 sur demande
Les tolérances en fil d'acier inoxydable pour usages généraux doivent faire l'objet d'un accord au moment de la commande ou de l'offre et peuvent être fournies en tolérances h6-h9.
TOLÉRANCES EN LONGUEUR STANDARD
| Longueur nominale | Tolérance |
| L < = 1000 mm | +/- 1 mm |
| 1000 < L < = 4000 | - 0 mm / +3 mm |
* Les données contenues dans ce site Web sont fournies à titre indicatif et ne constituent en aucune manière des conditions contractuelles de fourniture. Sauf erreur ou omission.
Wire 2024, held in Düsseldorf, marked a high point in the history of the wire and cable...
Contactez-nous