Acciaio inossidabile
COMPOSIZIONE CHIMICA. ANALISI DELLA FONDERIA (% in MASSA) EN-ISO 6931-1
| ACCIAIO INOSSIDABILE PER MOLLE | C | Si max. | Mn max. | P max. | S max. | Cr | Mo | Ni | Altri elementi | ||
| Designazione simbolica | Designazione numerica | AISI | |||||||||
| X10CrNi18-8 (NS / HS) | 1.4310 | 302 | 0,05 - 0,15 | 2,00 | 2,00 | 0,045 | 0,015 | 16,0 - 19,0 | ≤ 0,80 | 6,0 - 9,5 | N ≤ 0,11 |
| X5CrNiMo17-12-2 | 1.4401 | 316 | ≤ 0,07 | 1,00 | 2,00 | 0,045 | 0,015 | 16,5 - 18,5 | 2,00 - 2,50 | 10,0 - 13,0 | N ≤ 0,11 |
| X7CrNiAl17-7 | 1.4568 | 631 | ≤ 0,09 | 0,70 | 1,00 | 0,040 | 0,015 | 16,0 - 18,0 | - | 6,5 - 7,8 | Al: 0,70 - 1,50 |
| X5CrNi18-10 (NS / HS) | 1.4301 | 304 | ≤ 0,07 | 1,00 | 2,00 | 0,045 | 0,015 | 17,5 - 19,5 | - | 8,0 - 10,5 | N ≤ 0,11 |
| X1NiCrMoCu25-20-5 | 1.4539 | 904L | ≤ 0,020 | 0,70 | 2,00 | 0,030 | 0,010 | 19,0 - 21,0 | 4,0 - 5,0 | 24,0 - 26,0 | N ≤ 0,15 |
CHEMICAL COMPOSITION (HEAT ANALYSIS OF MARTENSITIC AND PRECIPITATION-HARDENED STAINLESS STEEL, FERRITIC STAINLESS STEEL AND AUSTENITIC STAINLESS STEEL) ACCORDING TO EN 10088-3
| ACCIAIO INOSSIDABILE PER USI GENERALI | % in massa | ||||||||||||
| Designazione simbolica | Designazione numerica | AISI | C | Si max. | Mn max. | P max. | S | N max. | Cr | Cu | Mo | Ni | Ti |
| Acciai Martensitici | |||||||||||||
| X30Cr13 | 1.4028 | 420 | 0,26 - 0,35 | 1,00 | 1,50 | 0,040 | ≤ 0,03 | - | 12,00- 14,00 | - | - | - | - |
| Acciai Ferritici | |||||||||||||
| X6Cr17 | 1.4016 | 430 | ≤ 0,08 | 1,00 | 1,00 | 0,04 | ≤ 0,030 | - | 16,00 - 18,00 | - | - | ≤ 0,75 | - |
| Acciai Austenitici | |||||||||||||
| X2CrNi18-9 | 1.4307 | 304L | ≤ 0,03 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 17,50 - 19,50 | - | - | 8,00 - 10,00 | - |
| X5CrNi18-10 | 1.4301 | 304 | ≤ 0,07 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 17,00 - 19,50 | - | - | 8,00 - 10,50 | - |
| X8CrNiS18-9 | 1.4305 | 303 | ≤ 0,10 | 1,00 | 2,00 | 0,045 | 0,15 - 0,35 | 0,11 | 17,00 - 19,00 | ≤ 1,00 | - | 8,00 - 1,00 | - |
| X2CrNiMo17-12-2 | 1.4401 | 316L | ≤ 0,03 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 16,50 - 18,50 | - | 2,00 - 2,50 | 10,00 - 13,00 | - |
| X2CrNiMo18-14-3 | 1.4435 | 316L | ≤ 0,03 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 17,00 - 19,00 | - | 2,50 - 3,00 | 12,50 - 15,00 | - |
| X5CrNiMo17-12-2 | 1.4401 | 316 | ≤ 0,07 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 16,50 - 18,50 | - | 2,00 - 2,50 | 10,00 - 13,00 | - |
| X3CrNiMo17-13-3 | 1.4436 | 316 | ≤ 0,05 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | 0,11 | 16,50 - 18,50 | - | 2,50 - 3,00 | 10,50 - 13,00 | - |
| X6CrNiMoTi17-12-2 | 1.4571 | 316Ti | ≤ 0,08 | 1,00 | 2,00 | 0,045 | ≤ 0,030 | - | 16,50 - 18,50 | - | 2,00 - 2,50 | 10,50 - 13,50 | 5 x C - 0,70 |
| X3CrNiCu18-9-4 | 1.4567 | 304Cu | ≤ 0,04 | 1,00 | 2,00 | 0,045 | ≤ 0,030 ³⁾ | 0,11 | 17,00 - 19,00 | 3,00 - 4,00 | - | 8,50 - 10,50 | - |
| X8CrMnCuNB17-8-3 | 1.4597 | 204Cu | ≤ 0,10 | ≤ 2,00 | 6,50 - 8,50 | ≤ 0,040 | ≤ 0,015 | - | 16,00 - 18,00 | 2,00 - 3,50 | ≤ 1,00 | ≤ 2,00 | - |
| X12CrNi23-13 | 1,4833 | 3095 | ≤ 0,08 | ≤ 0,75 | ≤ 2,00 | ≤ 0,040 | ≤ 0,015 | - | 22,00-24,00 | - | - | 12,00-14,00 | - |
| X8CrNi25-21 | 1,4845 | 310S | ≤ 0,08 | ≤ 1,50 | ≤ 2,00 | ≤ 0,040 | ≤ 0,015 | - | 24,00-26,00 | - | - | 19,00-22,00 | - |
| X15CrNiSi25-21 | 1.4841 | 314 | 0,02 | 1,50-3,00 | ≤ 0,02 | ≤ 0,045 | ≤ 0,015 | - | 24,00-26,00 | - | - | 19,00-22,00 | - |
| ACCIAIO INOSSIDABILE PER MOLLE | |||||
| Designazione simbolica | EN 10270-3 | AISI | EEUU ASTM | GIAPPONE JIS | CINA |
| X10CrNi18-8 | 1.4310 | 302NS | AISI 302 NS | SUS 302-WPB | - |
| X10CrNi18-8 | 1.4310 | 302HS | AISI 302 HLS | - | - |
| X5CrNiMo17-12-2 | 1.4401 | 316 | AISI 316 | SUS 316-WPA | - |
| X7CrNiAl17-7 | 1.4568 | 631 | AISI 631 | SUS 631J1-WPC | - |
| X5CrNi18-10 (NS / HS) | 1.4301 | 304 | AISI 304 | SUS 304-WPB | - |
| X1NiCrMoCu25-20-5 | 1.4539 | 904L | - | - | - |
| ACCIAIO INOSSIDABILE PER USI GENERAL | |||||
| Simbolica | Numerica EN 10088-3 | AISI | EEUU ASTM | GIAPPONE JIS | CINA |
| Tipos normalizados (Acciai Martensitici) 2) | |||||
|---|---|---|---|---|---|
| X30Cr13 | 1.4028 | 420 | |||
| Acciai Ferritici | |||||
| X6Cr17 | 1.4016 | 430 | |||
| Tipos normalizados (Acciai Austenitici) | |||||
| X2CrNi18-9 | 1.4307 | 304L | |||
| X5CrNi18-10 | 1.4301 | 304 | |||
| X8CrNiS18-9 | 1.4305 | 303 | |||
| X2CrNiMo17-12-2 | 1.4404 | 316L | |||
| X2CrNiMo18-14-3 | 1.4435 | 316L | |||
| X5CrNiMo17-12-2 | 1.4401 | 316 | |||
| X3CrNiMo17-13-3 | 1.4436 | 316 | |||
| X6CrNiMoTi17-12-2 | 1.4571 | 316Ti | |||
| X3CrNiCu18-9-4 | 1.4567 | 304Cu | |||
| X8CrMnCuNB17-8-3 | 1.4597 | 204Cu | |||
| X12CrNi23-13 | 1.4833 | 3095 | |||
| X8CrNi25-21 | 1.4845 | 310S | |||
| X15CrNiSi25-21 | 1.4841 | 314 | |||
RESISTENZA AL TRATTAMENTO NELLA CONDIZIONE DELL'ACCIAIO INOSSIDABILE TRATTATO PER MOLLE EN 10270-3
| Resistenza alla trazione (MPa) per i seguenti tipi di acciaio | |||||||||||||
| 1.4310 | 1.4401 | 1.4568 | 1.4301 | 1.4539 | |||||||||
| Diametro nominale mm d | 302NS | 302HS | 316 | 631 | 304NS | 304HS | 904L | ||||||
| min. | max. | min. | max. | min. | max. | min. | max. | min. | min. | max. | min. | max. | |
| d ≤ 0,20 | 2200 | 2530 | 2350 | 2710 | 1725 | 1990 | 1975 | 2280 | 2000 | 2150 | 2300 | 1600 | 1840 |
| 0,20 < d ≤ 0,30 | 2150 | 2480 | 2300 | 2650 | 1700 | 1960 | 1950 | 2250 | 1975 | 2050 | 2280 | 1550 | 1790 |
| 0,30 < d ≤ 0,40 | 2100 | 2420 | 2250 | 2590 | 1675 | 1930 | 1925 | 2220 | 1925 | 2050 | 2220 | 1550 | 1790 |
| 0,40 < d ≤ 0,50 | 2050 | 2360 | 2200 | 2530 | 1650 | 1900 | 1900 | 2190 | 1900 | 1950 | 2190 | 1500 | 1750 |
| 0,50 < d ≤ 0,65 | 2000 | 2300 | 2150 | 2480 | 1625 | 1870 | 1850 | 2130 | 1850 | 1950 | 2130 | 1450 | 1670 |
| 0,65 < d ≤ 0,80 | 1950 | 2250 | 2100 | 2420 | 1600 | 1840 | 1825 | 2100 | 1800 | 1850 | 2070 | 1450 | 1670 |
| 0,80 < d ≤ 1,00 | 1900 | 2190 | 2050 | 2360 | 1575 | 1820 | 1800 | 2070 | 1775 | 1850 | 2050 | 1400 | 1610 |
| 1,00 < d ≤ 1,25 | 1850 | 2130 | 2000 | 2300 | 1550 | 1790 | 1750 | 2020 | 1725 | 1750 | 1990 | 1350 | 1560 |
| 1,25 < d ≤ 1,50 | 1800 | 2070 | 1950 | 2250 | 1500 | 1730 | 1700 | 1960 | 1675 | 1750 | 1930 | 1350 | 1560 |
| 1,50 < d ≤ 1,75 | 1750 | 2020 | 1900 | 2190 | 1450 | 1670 | 1650 | 1900 | 1625 | 1650 | 1870 | 1300 | 1500 |
| 1,75 < d ≤ 2,00 | 1700 | 1960 | 1850 | 2130 | 1400 | 1610 | 1600 | 1840 | 1575 | 1650 | 1820 | 1300 | 1500 |
| 2,00 < d ≤ 2,50 | 1650 | 1900 | 1750 | 2020 | 1350 | 1560 | 1550 | 1790 | 1525 | 1550 | 1760 | 1300 | 1500 |
| 2,50 < d ≤ 3,00 | 1600 | 1840 | 1700 | 1960 | 1300 | 1500 | 1500 | 1730 | 1475 | 1550 | 1700 | 1300 | 1500 |
| 3,00 < d ≤ 3,50 | 1550 | 1790 | 1650 | 1900 | 1250 | 1440 | 1450 | 1670 | 1425 | 1450 | 1640 | 1300 | 1500 |
| 3,50 < d ≤ 4,25 | 1500 | 1730 | 1600 | 1840 | 1225 | 1410 | 1400 | 1610 | 1400 | 1450 | 1610 | 1250 | 1440 |
| 4,25 < d ≤ 5,00 | 1450 | 1670 | 1550 | 1790 | 1200 | 1380 | 1350 | 1560 | 1350 | 1350 | 1560 | 1250 | 1440 |
| 5,00 < d ≤ 6,00 | 1400 | 1610 | 1500 | 1730 | 1150 | 1330 | 1300 | 1500 | 1300 | 1350 | 1500 | 1250 | 1440 |
| 6,00 < d ≤ 7,00 | 1350 | 1560 | 1450 | 1670 | 1125 | 1300 | 1250 | 1440 | 1250 | 1300 | 1440 | 1200 | 1380 |
| 7,00< d ≤ 8,50 | 1300 | 1500 | 1400 | 1610 | 1075 | 1240 | 1250 | 1440 | 1200 | 1300 | 1380 | 1150 | 1330 |
| 8,50 < d ≤ 10,00 | 1250 | 1440 | 1350 | 1560 | 1050 | 1210 | 1250 | 1440 | 1175 | 1250 | 1360 | - | - |
NOTA - Possibilità di fornitura di d ≥ 14mm fuori standard, previa richiesta commerciale.
TENSILE STRENGTH RANGE IN EACH UNIT PACKAGE (REEL, COIL, PACKAGE) EN 10270-3
| Diametro di filo d (mm) | Intervalo máximo |
| d ≤ 1,50 | 100 |
| 1,50 < d ≤ 10,00 | 70 |
ACCIAIO PER VARIE APPLICAZIONI
| Simbolica | Numerica EN 10088-3 | AISI | Resistenza [N/mm2] | |
| Stato Ricotto | Stato Semi-Crudo | |||
| X6Cr17 | 1.4016 | 430 | ≤ 640 | 650-900 |
| X2CrNi18-9 | 1.4307 | 304L | ≤ 640 | 650-900 |
| X5CrNi18-10 | 1.4301 | 304 | ≤ 640 | 650-900 |
| X8CrNiS18-9 | 1.4305 | 303 | ≤ 590 | 600-700 |
| X3CrNiCu18-9-4 | 1.4567 | 304Cu | ≤ 600 | 600-700 |
QUALITÀ SUPERFICIALE EN-ISO 6931-1
La superficie del filo deve essere liscia e il più possibile libera da graffi, ABRASIONI e altri difetti superficiali che potrebbero compromettere l’uso del filo. Un metodo che rivela le discontinuità superficiali è il test di torsione alternativa.
Se il filo è destinato alla produzione di molle che vengono utilizzate con forti sollecitazioni, i requisiti speciali relativi alla qualità della superficie e ai test possono essere concordati previa indicazione del cliente al momento della richiesta dell’offerta o dell’ordine.
| Finiture Superficiali per Fili per Molle: | |
| Stearato S-Co | Rivestimento standard |
| Stearato speciale SS-Co / S-Co+ | Migliora la conformazione della molla |
| Lucidato | Aspetto superficiale lucido, anche se c’è un leggero strato di sapone |
| Polido | Trafilatura bagnata |
| Nichelatura Opaca | Trafilatura a secco |
| Nichelatura Lucida | Trafilatura bagnata |
QUALITÀ SUPERFICIALE EN 10088-3
Sono tollerate lievi irregolarità superficiali, inerenti al processo di fabbricazione. Se necessario, i requisiti più precisi relativi alla qualità della superficie possono essere concordati al momento dell’ordine, in base alla norma EN 10221.
TOLLERANZE NEL DIAMETRO EN-ISO 6931-1
| Diametro nominale d (mm) | Tolerâncias no diâmetro (mm) | |
| Carretéis ou bobinas | ||
| T14 | T15 | |
| d ≤ 0,20 | ± 0,005 | ± 0,004 |
| 0,20 < d ≤ 0,25 | ± 0,005 | ± 0,004 |
| 0,25 < d ≤ 0,40 | ± 0,008 | ± 0,005 |
| 0,40 < d ≤ 0,64 | ± 0,008 | ± 0,005 |
| 0,64 < d ≤ 0,80 | ± 0,010 | ± 0,008 |
| 0,80 < d ≤ 1,00 | ± 0,010 | ± 0,008 |
| 1,00 < d ≤ 1,60 | ± 0,015 | ± 0,010 |
| 1,60 < d ≤ 2,25 | ± 0,015 | ± 0,010 |
| 2,25 < d ≤ 3,19 | ± 0,020 | ± 0,015 |
| 3,19 < d ≤ 4,00 | ± 0,020 | ± 0,015 |
| 4,00 < d ≤ 4,50 | ± 0,025 | ± 0,020 |
| 4,50 < d ≤ 6,00 | ± 0,025 | ± 0,020 |
| 6,00 < d ≤ 6,25 | ± 0,025 | ± 0,020 |
| 6,25 < d ≤ 7,00 | ± 0,030 | ± 0,025 |
| 7,00 < d ≤ 9,00 | ± 0,030 | ± 0,025 |
| 9,00 < d ≤ 10,00 | ± 0,035 | ± 0,030 |
NOTA 1 - Possibilità di fornitura di d ≥ 14mm fuori standard, previo accordo commerciale.
NOTA 2 - T15 su richiesta.
Le tolleranze del filo di acciaio inossidabile per uso generale devono essere concordate al momento dell’ordine o dell’offerta e possono essere fornite con tolleranze h6-h9.
TOLERÂNCIAS DE COMPRIMENTO STANDARD
| LUNGHEZZA NOMINALE | TOLLERANZA |
| L < = 1000 mm | +/- 1 mm |
| 1000 < L < = 4000 | - 0 mm / +3 mm |
* I dati contenuti nella presente pagina web sono meramente informativi e non costituiscono, in nessun caso, condizioni contrattuali di fornitura. Salvo errore od omissione.
Wire 2024, held in Düsseldorf, marked a high point in the history of the wire and cable...
Consultaci